| ngoi-kôn |
|---|
silvery white
 |
| Kî-pún sin-sit |
|---|
| Miàng, fù-ho |
Dysprosium, Dy |
|---|
| ngoi-hìn |
silvery white |
|---|
| Dysprosium chhai chû-khì-péu ke vi-chi |
|---|
|
|
| ngièn-chṳ́ sì-sú |
66 |
|---|
| ngièn-chṳ́-liòng (±) |
162.500(1)[1] |
|---|
| ngièn-su lui-phe̍t |
lanthanum-hi |
|---|
| Chhu̍k, fûn-khî |
n/a, f-block |
|---|
| chû-khì |
period 6 |
|---|
| thien-chṳ́ phài-lie̍t |
[Xe] 4f10 6s2 |
|---|
| per shell |
2, 8, 18, 28, 8, 2 |
|---|
| vu̍t-lî sin-chṳt |
|---|
| Siông |
ku-thí |
|---|
| yùng-tiám |
1680 K (1407 °C, 2565 °F) |
|---|
| pui-tiám |
2840 K (2562 °C, 4653 °F) |
|---|
| Me̍t-thu near Sit-vûn |
8.540 g·cm−3 |
|---|
|
8.37 g·cm−3 |
| Yùng-fa-ngie̍t |
11.06 kJ·mol−1 |
|---|
| Chîn-fat-ngie̍t |
280 kJ·mol−1 |
|---|
| Ngie̍t-yùng-liong |
27.7 J·mol−1·K−1 |
|---|
chîn-hi-ap
| P (Pa)
|
1
|
10
|
100
|
1 k
|
10 k
|
100 k
| | chhai T (K)
|
1378
|
1523
|
(1704)
|
(1954)
|
(2304)
|
(2831)
|
|
| Ngièn-chṳ́ sin-chṳt |
|---|
| Yông-fa-su |
4, 3, 2, 1 (a weakly basic oxide) |
|---|
| Thien-fu-sin |
Pauling scale: 1.22 |
|---|
| Thien-lì-nèn |
1st: 573.0 kJ·mol−1
2nd: 1130 kJ·mol−1
3rd: 2200 kJ·mol−1 |
|---|
| Ngièn-chṳ́ pan-kang |
empirical: 178 pm |
|---|
| Khiung-ka pan-kang |
192±7 pm |
|---|
| Miscellanea |
|---|
| Chîn-thí keu-chho |
hexagonal close-packed (hcp) |
|---|
| Sâng-suk thin rod |
2710 m·s−1 (at 20 °C) |
|---|
| Ngie̍t-phàng-chong |
α, poly: 9.9 µm·m−1·K−1 (r.t.) |
|---|
| Ngie̍t-chhòn-thô-li̍t |
10.7 W·m−1·K−1 |
|---|
| Thien-chú-li̍t |
α, poly: 926 nΩ·m (r.t.) |
|---|
| Chhṳ̀-sin |
paramagnetic at 300 K |
|---|
| Young's modulus |
α form: 61.4 GPa |
|---|
| Shear modulus |
α form: 24.7 GPa |
|---|
| Bulk modulus |
α form: 40.5 GPa |
|---|
| Poisson ratio |
α form: 0.247 |
|---|
| Vickers hardness |
410–550 MPa |
|---|
| Brinell hardness |
500–1050 MPa |
|---|
| CAS Registry Number |
7429-91-6 |
|---|
| Le̍k-sú |
|---|
| Fat-hien |
Lecoq de Boisbaudran (1886) |
|---|
| Chui vún-thin ke thùng-vi-su |
|---|
|
Chú vùn-chông: Dysprosium ke thùng-vi-su |
| iso
|
NA
|
half-life
|
DM
|
DE (MeV)
|
DP
|
|---|
| 154Dy
|
syn
|
3.0×106 y
|
α
|
2.947
|
150Gd
| | 156Dy
|
0.06%
|
>1×1018 y
|
(α)
|
1.7579
|
152Gd
| | (β+β+)
|
2.0108
|
156Gd
| | 158Dy
|
0.10%
|
–
|
(α)
|
0.8748
|
154Gd
| | (β+β+)
|
0.2833
|
158Gd
| | 160Dy
|
2.34%
|
–
|
(α)
|
0.4387
|
156Gd
| | 161Dy
|
18.91%
|
–
|
(α)
|
0.3443
|
157Gd
| | 162Dy
|
25.51%
|
–
|
(α)
|
0.0847
|
158Gd
| | 163Dy
|
24.90%
|
–
|
(SF)
|
<79.055
|
| | 164Dy
|
28.18%
|
–
|
(SF)
|
<79.499
|
|
|
|
Decay modes in parentheses are predicted, but have not yet been observed |